@article{oai:toyama.repo.nii.ac.jp:00004525,
 author = {蓮覚寺, 聖一 and 向畠, 眞一郎 and 中村, 優子 and 平田, 貴之},
 journal = {富山大学工学部紀要},
 month = {Feb},
 note = {The effect of the pulsing current on the composition and strain of Ni-Mo alloys pulse-plated from acidic citrate bath was investigated. The molybdenum content increased with increasing molybdate ion concentration in the bath, and the increasing tendency of molybdenum varied with a peak current density. The molybdenum content was not dependent on a pulse frequency, therefore the strain in deposits was not affect by pulse frequency. Comparing with the cracks in deposits obtained from D.C.-plating, the cracks were reduced by the applying pulse-plating conditions such as the pulse frequencies of 10 and 20Hz. The surface of deposits pulse-plated was smoother than that of D.C.-plated surface., 酸性クエン浴から電着するNi-Mo合金の組成や電着歪みにパルス電流が及ぼす影響について検討した。Mo含有率はモリブデン酸イオン濃度が高くなるにつれ増加し，その増加傾向はピーク電流密度によって変化した。またMo含有率はパルス周波数に依存しなかった。それゆえ析出物中の電着歪みはパルス周波数によっても影響されなかった。パルス周波数10，20Hzの条件下でパルスめっきを行なうと析出物のクラックは直流めっきの場合と比較して減少した。また，パルスめっきによって得られた電着物の表面は直流めっきのそれよりも平滑となった。, Article, 富山大学工学部紀要，47, Page 89-95},
 pages = {89--95},
 title = {パルスめっきによる酸性クエン酸浴からのNi-Mo合金の電着歪みについて},
 volume = {47},
 year = {1996}
}