 note = {application/pdf, In order to investigate the effects of various factors on serrated yield, tensile tests were performed on A-l-0.5--70wt%Mg alloys.
Three type of serrated yield named Type A, B and C were distingu ished.
The values of actviation energy for Type A serrated yield were found to be 0.24--0.33 eV, which were independent on grain size.
Type B serrated yield was appeared at middile temperatures, and Type C serrated yield at higher temperatures.
The mechanism for onset of both B and C Type serrated yield were explained qualitatviely as the propergation of luders band due to stress concentration at grain boundary., Al-0.5～7.0wt%Mg合金のセレーションに対する種々の因子の影響を引張り試験により調べた。
その結果，セレーションはA，B及びC型の3種類に大別された。
A型セレーションの活性化エネルギーは0.24～0.33eVであり，結晶粒度によっては変化しなかった。
B型セレーションは中間温度範囲で生じ，C型セレーションは最も高い温度領域で生じた。B及びC型セレーションはいずれも結晶粒界における堆積転位の応力集中によりリューダース帯が伝播する事により生ずると定性的に説明された。, Article, 富山大学工学部紀要，37},