 note = {The deformation of bearing steel JIS SUJ3 specimens under the repeated blow is studied, by the same method in my previous report [Bulletin of Faculty of Eng. Toyama University, Vol. 20 (1969)]. The test temperature is 100℃ and 150℃ and the number of blows is 6 x 10^4, 12 x 10^4 and 18 x 10^4. 
The deformation of the specimen, sub-zero treated or marquenched, is 30--40% smaller than that of the norma1 heat treated specimen, and also smaller than that of the steel JIS SUJ2 specimen (refer to my previous report). The author presumes that these results are caused by the martensite transformation of the retained allstenite under stress of the blow and the tempering of that martensite of the specimens heated under the test., ころがり軸受が使用されるときには，繰返し荷重が加り，叉摩擦によって温度が上昇するので，軸受が変形を起すが，その変形量が大きいときには，軸受の機能に相当の影響が生ずるので，変形量の少いことが望ましい。
サブゼロ処理を施せば，経年変形を少くすることが出来るが，同時にこのような加工変形に対しても抵抗の大きいことが期待される。
本報告では，前回の鋼種SUJ2（軸受鋼第2種）に引つづき，鋼種SUJ3について，更に温度が上昇した場合について，変形を比較検討した。, Article, 富山大学工学部紀要，21},
 pages = {103--107},
 title = {繰返打撃変形に対するサブゼロ処理の効果について(II)},
 volume = {21},
 year = {1970}
}