@article{oai:toyama.repo.nii.ac.jp:00003335,
 author = {Ishihara, Sotomi and Maekawa, Ichiro and Shiozawa, Kazuaki and Miyao, Kazyu},
 issue = {240},
 journal = {Bulletin of JSME},
 month = {Jun},
 note = {application/pdf, Many small distributed cracks have been observed on the specimen during corrosion fatigue process, and the damage of corrosion fatigue is related to the behaviour of these distributed cracks. The distribution of crack lengths during corrosion fatigue was approximated well by the three parameter Weibull distribution under plane-bending fatigue tests of carbon steel in salt water. A method of estimation of corrosion fatigue lives was proposed. The crack initiation, crack growth behaviour and the variation of the distribution of crack lengths during corrosion fatigue process were taken into consideration in the method. Comparing the estimated results with experimental results, it was concluded that this method could estimate the corrosion fatigue lives with good accuracy., Article},
 pages = {1015--1022},
 title = {Estimation of Corrosion Fatigue Lives Based on the Variations of the Crack Lengths Distributions During Stress Cycling},
 volume = {28},
 year = {1985}
}