@article{oai:toyama.repo.nii.ac.jp:00003281,
 author = {石原, 外美 and 塩澤, 和章 and 宮尾, 嘉寿 and 神島, 裕児},
 issue = {523},
 journal = {日本機械学會論文集. A編 = Transactions of the Japan Society of Mechanical Engineers. A},
 month = {Mar},
 note = {application/pdf, In order to investigate variations of spatial distributions of cracks observed on the unnotched specimen surface during the fatigue process, plane bending fatigue tests were performed on carbon steel JIS, SS 41 in laboratory air and a sodium chloride aqueous solution. Two methods, developed by Morishita and Ono in the field of mathematical ecology, were used in analyzing the spatial distributions of Cracks. The following results were obtained. The spatial distributions of cracks are influenced by both stress amplitude and stress cycling. In the high stress amplitude region, the distributions are nearly random, while in the low stress amplitude region, the distributions have clumps indicating nonrandom distribution. This result was common to both fatigue in air and corrosion fatigue. With increasing stress cycling, the spatial distributions of cracks approach random distributions in the high stress amplitude region, while in the low stress amplitude region, the distributions show a strong tendency to have two kinds of clumps whose sizes are 1/4 mm^2 and 8 mm^2., Article},
 pages = {494--500},
 title = {炭素鋼平滑試験片の平面曲げ疲労過程における複数き裂の空間分布 : 応力振幅および繰返し数依存性},
 volume = {56},
 year = {1990}
}